Sn/C纳米复合材料的合成及其电化学嵌放锂性能
李辉1,2,李赫1,3,常焜1,陈卫祥1
1.浙江大学 化学系,浙江 杭州 310027; 2. 湖州微宏动力系统有限公司,浙江 湖州 313000;
3.浙江树人大学 生物与环境学院,浙江 杭州 310015
Synthesis of Sn/C nanocomposites and their
electrochemical performances as anode materials of Li-ion battery
LI Hui1,2, LI He1,3 , CHANG Kun1, CHEN Wei-xiang1
1.Department of Chemistry, Zhejiang University, Hangzhou 310027, China;
2. Microvast Power System Co., Ltd., Huzhou 313000, China;
3. College of Biology and Environmental Engineering, Zhejiang Shuren University, Hangzhou 310015, China
 全文: PDF  HTML
摘要:

用SnCl4和葡萄糖的水热反应合成SnO2/碳质复合材料,然后在氮气气氛中热处理使SnO2被碳热还原为Sn纳米粒子,制备得到Sn/C纳米复合材料.用X-射线衍射(XRD), 透射电镜(TEM)和X-射线电子散射能谱(EDX)对样品进行表征.结果显示Sn纳米粒子具有球形的形貌,并均匀地分散在无定形的碳材料中.对于Sn质量分数58.5%和32.3%的Sn/C复合材料,Sn纳米粒子的平均粒径分别为51和20 nm.电化学测试结果显示,Sn/C复合材料具有高的电化学贮锂可逆容量和良好的循环稳定性.讨论了Sn/C纳米复合材料的形成机理及其循环稳定性能改善的原因.

Abstract:

The SnO2/carbonaceous composites were firstly prepared by the hydrothermal reaction between SnCl4 and glucose. Sn/C nanocomposites were obtained after the treatment of the SnO2/carbonaceous composites in N2 gas flow, during which SnO2 was reduced to Sn nanoparticles by carbon thermal reduction. The products were characterized by XRD, TEM and EDX. The results shows that the Sn nanoparticles are spherical and dispersed in amorphous carbon materials. The mean diameters of Sn nanoparticles are 51 nm and 20 nm, respectively, for the Sn/C composites with Sn of 58.5wt% and 32.3wt%. Electrochemical tests demonstrate that the Sn/C nanocomposite electrodes exhibit high reversible capacity and good cycling performances used as anode materials of Li-ion battery. The mechanisms of the formation of Sn/C nanocomposites and the improvement in their cycling performances were also investigated.

出版日期: 2011-11-24
:  TM 911  
基金资助:

浙江省自然科学基金资助项目(Y4100119);浙江省科技厅公益性资助项目(2011C31G2010027);国家重点基础研究发展计划“973”资助项目(2010CB635116).

通讯作者: 陈卫祥, 男, 教授, 博导.     E-mail: weixiangchen@zju.edu.cn
作者简介: 李辉(1978-), 男, 山东济宁人, 博士, 从事电极材料和化学电源研究.
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
作者相关文章  

引用本文:

李辉,李赫,常焜,陈卫祥. Sn/C纳米复合材料的合成及其电化学嵌放锂性能[J]. J4, 2011, 45(5): 919-922.

LI Hui, LI He, CHANG Kun, CHEN Wei-xiang. Synthesis of Sn/C nanocomposites and their
electrochemical performances as anode materials of Li-ion battery. J4, 2011, 45(5): 919-922.

链接本文:

https://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2011.05.024        https://www.zjujournals.com/eng/CN/Y2011/V45/I5/919

[1] IDOTA Y, KUBOTA T, MATSUFUJI A, et al. Tinbased amorphous oxide: a highcapacity lithiumionstorage material [J]. Science, 1997, 276(5317): 1395-1397.

[2] BROUSSE T, RETOUX R, HERTERICH U, et al. Thinfilm crystalline SnO2lithium electrodes [J]. Journal of The Electrochemical Society, 1998, 145(1): 1-4.
[3] ZUO P, YIN G, MA Y. Electrochemical stability of silicon/carbon composite anode for lithium ion batteries [J]. Electrochimica Acta, 2007, 52(6): 4878-4883.
[4] WEN ZS, YANG J, WANG BF, et al. High capacity silicon/carbon composite anode materials for lithium ion batteres \
[J\] .Electrochenistry Communications, 2003, 5(2): 165-168.
[5] Derrien G, Hassoun J, Panero S, et al. Nanostructured SnC composite as an advanced anode material in highperformance lithiumIon Batteries [J]. Advanced Materials, 2007, 19(3): 2336-2340.
[6] HASSOUN J, DERRIEN G, PANERO S, et al. Nanostructured SnC composite lithium battery electrode with unique stability and high electrochemical performance [J]. Advanced Materials, 2008, 20(16): 3169-3175.
[7] GUO CX, CAO MH, HU CW, A novel and lowtemperature hydrothermal synthesis of SnO2 nanorods [J] Inorganic Chemistry Communications, 2004, 21(7): 929-931.
[8] SUN XM, LI YD. Colloidal carbon spheres and their core/shell structures with noblemetal nanoparticles [J]. Angewandte Chemie International Edition, 2004, 116(5): 597-601.
[9] SUN X X, LIU J F, LI Y D. Oxides@C coreshell nanostructures: onepot synthesis, rational conversion, and Li storage property [J]. Chemistry of Materials, 2006, 18(15): 3486-3494.
[10] HUANG X H, TU J P,ZHANG C Q,et al.Netstructured NiOC nanocomposite as Liintercalation electrode material [J].Electrochemistry Communication, 2007, 9(5):1180-1184.
[11] GUO H, ZHAO H, JIA X, et al. A novel microspherical CoSn2/Sn alloy composite as high capacity anode materials for Liion rechargeable batteries [J]. Electrochimica Acta, 2007, 52(14): 4853-4857.

[1] 马琳,肖玉凤,赵杰,陈卫祥. 中空Pd/C催化剂的合成及其对甲酸氧化电催化性能[J]. J4, 2011, 45(5): 923-927.
[2] 马琳, 李辉, 常焜, 李赫, 陈卫祥. 水热合成纳米片状SnS2及其电化学贮放锂性能[J]. J4, 2011, 45(2): 354-357.
[3] 管成, 王向炜, 王冬云. 混合动力挖掘机用镍氢电池SOC估算策略[J]. J4, 2010, 44(12): 2370-2375.