基于DIC技术的锈蚀钢筋混凝土表面开裂
童晶, 金贤玉, 田野, 金南国
浙江大学 建筑工程学院,浙江 杭州 310058
Study on surface cracking of corroded reinforced concrete based on DIC method
TONG jing, JIN Xian yu, TIAN Ye, JIN Nan guo
College of Civil Engineering and Architecture, Zhejiang University, Hangzhou 310058,China
 全文: PDF(2319 KB)   HTML
摘要：

为研究钢筋混凝土梁混凝土保护层锈胀开裂的全过程,基于数字图像相关(DIC)技术,采用数字散斑图像的匹配追踪分析方法,揭示氯盐环境中外加电流加速锈蚀条件下钢筋混凝土梁表面广义主应变场的时变演化规律.结果表明：混凝土梁内纵筋与箍筋的锈蚀均对试件表面的广义主应变分布场产生影响,并且锈蚀混凝土梁表面纵向初裂位置附近的广义主应变分布具有圣维南特性；使用DIC技术可以准确判断混凝土梁表面初始开裂的时间、位置以及裂纹的走向.研究方法与成果对于量化表征钢筋混凝土结构的锈蚀开裂全过程具有重要意义.
Abstract:

In order to analyze the whole corrosion cracking process of the cover on reinforced concrete beams, the development of generalized principle strain field on the surface of reinforced concrete beams under accelerated corrosion due to impressed current in chlorides environment was investigated through a matching pursuit processing on the digital speckle image based on digital image correlation (DIC) technology. The results indicate that the corrosion of longitudinal steel bars and stirrups in the beam both influence the generalized principle strain field on the surface of specimens. And Saint-Venant characteristics can be recognized from the distribution of generalized principle strain within the longitudinal initial cracking zone on the corroded reinforced concrete beam. DIC technology can precisely reflect the time, location and trend of cracking generation on the surface of concrete. The research method and results of this research are of great importance for the quantitative characterization on the whole cracking process due to corrosion of reinforced concrete structure.
出版日期: 2015-02-01
:  TU 528  
基金资助:

国家“973”重点基础研究发展规划资助项目（2015CB655103）；国家自然科学基金资助项目（51478419,51378012）
通讯作者: 田野,男,副教授，硕导     E-mail: cetianye@zju.edu.cn
作者简介: 童晶(1990—), 女, 硕士生, 从事混凝土耐久性研究. E-mail: tongjing199010@163.com
服务　　
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章　　

引用本文:

童晶, 金贤玉, 田野, 金南国. 基于DIC技术的锈蚀钢筋混凝土表面开裂[J]. 浙江大学学报(工学版), 10.3785/j.issn.1008-973X.2015.02.001.

TONG jing, JIN Xian yu, TIAN Ye, JIN Nan guo. Study on surface cracking of corroded reinforced concrete based on DIC method. JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 10.3785/j.issn.1008-973X.2015.02.001.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2015.02.001    或    http://www.zjujournals.com/eng/CN/Y2015/V49/I2/193

［1］ SUDA K, MISRA S, MOTOHASHI K. Corrosion products of reinforced bars embedded in concrete ［J］. Corrosion Science, 1993, 35(5/8): 1543-1549.
［2］ ZHAO Yu-xi, REN Hai-yang, DAI Hong. Composition and expansion coefficient of rust based on X-ray diffraction and thermal analysis ［J］.Corrosion Science, 2011, 53(1): 1646-1658.
［3］ ANDRADE C, ALONSO C, MOLINA F J. Cover cracking as a function of bar corrosion: Part 1-experimental test ［J］. Materials and Structures, 1993, 26(8): 453-464.
［4］ ALONSO C, ANDRADE C, RODRIGUEZ J. Factors controlling cracking of concrete affected by reinforcement corrosion ［J］. Materials and Structures, 1998, 31(8/9): 435-441.
［5］ RASHEEDUZZAFAR,AL-SAADOUN S S,AL-GAHTANI A S. Corrosion cracking in relation to bar diameter, cover, and concrete quality ［J］. Journal of Materials in Civil Engineering,1992, 4(4)： 327-342.
［6］ MALUMBELA G, MOYO P,ALEXANDER M . Lateral deformation of RC beams under simultaneous load and steel corrosion ［J］. Construction and Building Materials, 2010, 24(1): 17-24.
［7］ MALUMBELA G, ALEXANDER M, MOYO P. Influence of corrosion crack patterns on the rate of crack widening of RC beams ［J］. Construction and Building Materials,2011, 25(5): 2540-2553.
［8］ MALUMBELA G, MOYO P,ALEXANDER M .Behaviour of RC beams corroded under sustained service loads ［J］. Construction and Building Materials, 2009, 23(11):3346-3351.
［9］ MALUMBELA G, MOYO P, ALEXANDER M . Longitudinal strains and stiffness of RC beams under load as measures of corrosion levels ［J］.Engineering Structures, 2012, 35: 215-227.
［10］ YAMAGUCHI I.A laser-speckle strain gauge ［J］.Journal of Physics(E):Scientific Instruments, 1981, 14(5): 1270-1273.
［11］ PETERS W H, RANSON W F. Digital imaging techniques in experimental stress analysis ［J］.Optical Engineering, 1982, 21(3): 427-431.
［12］ LAWLER J S, KEANE D T, SHAH S P. Measuring three-dimensional damage in concrete under compression ［J］. Materials Journal, 2001,98(6): 465-475.
［13］ 刘宁,赵颖华,金观昌.碳纤维布加固钢筋混凝土梁的DSCM实验研究［J］.工程力学,2004,21（4）： 179-183.
LIU Ning, ZHAO Ying-hua, JIN Guan-chang. Experimental study of concrete beams strengthened with carbon fiber sheet using digital speckle correlation method ［J］. Engineer Mechanics, 2004, 21（4）： 179-183.
［14］ GUO Li-ping, SUN Wei, HE Xiao-yuan. Application of DSCM in prediction of potential fatigue crack path on concrete surface ［J］. Engineering Fracture Mechanics, International Conference in Crack Paths, 2008, 75(3/4): 643-651.
［15］ GUO Li-ping, SUN Wei, CARPINTERI A. Latent crack path and service life predictions for unnotched concrete under bending by digital speckle correlation method ［J］.Fatigue and Fracture of Engineering Materials and Structures, 2008, 31(1): 29-37.
［16］ HELM J D.Digital image correlation for specimens with multiple growing cracks ［J］. Experimental Mechanics, 2008, 48(6): 753-762.
［17］ 潘兵,谢惠民.数字图像相关中基于位移场局部最小二乘拟合的全场应变测量［J］. 光学学报,2007,27(11): 1980-1986.
PAN Bing,XIE Hui-min.Full-field Strain Measurement Based on least-square fitting of local displacement for digital image correlation method ［J］.Acta Optica Sinica, 2007,27(11): 1980-1986.
［18］ LU H , CARY P D.Deformation measurements by digital image correlation: implementation of a second-order displacement gradient ［J］.Experimental echanics,2000,40(4): 393-400.
［19］ SUN Zili, LYONS J S, MCNEILL S R. Measuring microscopic deformations with digital image correlation ［J］.Optics and Lasers in Engineering,1997,27(4): 409-428.
［20］ 徐世烺. 混凝土断裂力学［M］. 北京：科学出版社,2011, 439-450.
［21］ MALUMBELA G, ALEXANDER M,MOYO P .Interaction between corrosion crack width and steel loss in RC beams corroded under load ［J］.Cement and Concrete Research, 2010, 40(9)： 1419-1428.
[1] 欧祖敏, 孙璐. 冻融损伤混凝土的弯曲疲劳寿命可靠性分析[J]. 浙江大学学报(工学版), 2017, 51(6): 1074-1081.
[2] 李静, 王哲. 似平面应力条件下混凝土的变形特性[J]. 浙江大学学报(工学版), 2017, 51(4): 745-751.
[3] 温小栋, 蔡煜梁, 赵莉, 冯蕾. 凝灰岩机制砂混凝土抗低温硫酸盐侵蚀性[J]. 浙江大学学报(工学版), 2017, 51(3): 532-537.
[4] 熊海贝,曹纪兴,张凤亮. 含加强层框筒结构位移监测方法[J]. 浙江大学学报(工学版), 2016, 50(9): 1752-1760.
[5] 吴萌, 姬永生, 陈晓峰, 张领雷, 陈向东. 超细粉煤灰对碳硫硅钙石型硫酸盐破坏的影响[J]. 浙江大学学报(工学版), 2016, 50(8): 1479-1485.
[6] 熊海贝, 李奔奔, 江佳斐. FRP约束混凝土圆柱应力-应变模型的适用性[J]. 浙江大学学报(工学版), 2015, 49(12): 2363-2375.
[7] 段安, 张大伟, ALNAGGAR Mohammed. 微平面模型模拟ASR作用下混凝土力学行为[J]. 浙江大学学报(工学版), 2015, 49(10): 1939-1945.
[8] 杜明月, 田野, 金南国, 王宇纬, 金贤玉. 基于水泥水化的早龄期混凝土温湿耦合[J]. 浙江大学学报(工学版), 2015, 49(8): 1410-1416.
[9] 姚晓莉, 易思阳, 范利武, 徐旭, 俞自涛, 葛坚. 不同孔隙率下含湿加气混凝土的有效导热系数[J]. 浙江大学学报(工学版), 2015, 49(6): 1101-1107.
[10] 王雪松, 金贤玉, 田野, 李蓓, 金南国. 开裂混凝土中钢筋加速锈蚀方法适用性[J]. J4, 2013, 47(4): 565-574.
[11] 陈军, 金南国, 金贤玉, 洪天从. 基于电阻率法研究混凝土渗透性能演变规律[J]. J4, 2013, 47(4): 575-580.
[12] 俞可权, 陆洲导, 唐安静.
高温后混凝土断裂全过程的裂缝扩展阻力曲线[J]. J4, 2013, 47(4): 588-594.
[13] 谢中凯,刘国华. 近似熵在混凝土结构损伤识别中的应用[J]. J4, 2013, 47(3): 456-464.
[14] 王雪松, 金贤玉, 田野, 金南国. 基于非均匀锈蚀的带肋钢筋黏结性能[J]. J4, 2013, 47(1): 154-161.
[15] 谢中凯, 刘国华, 吴志根. 基于传递熵的梁结构损伤动力识别[J]. J4, 2012, 46(10): 1880-1886.