Microstructure and creep properties of high Cr resisting weld metal alloyed with Co |
Xue Wang, Liang-fei Zhan, Qian-gang Pan, Zhi-jun Liu, Hong Liu, Yong-shun Tao |
School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072, China, DongFang Boiler Group Co. Ltd., Zigong 643001, China |
|
|
Abstract A 9% Cr ferritic steel weld metal containing 1% Co, partially substituted for nickel, was prepared by submerged arc welding (SAW) processing. The microstructure and creep properties of the weld metal were investigated. The microstructure exhibited a fully tempered martensitic structure free of δ-ferrite. The creep properties of the obtained weld metal were inferior to those of the P92 base metal at 600 and 650 °C. The values of A and n for weld metal in the Norton power law constitution at 650 °C are 1.1×10−21 and 8.1, respectively.
|
Received: 06 May 2010
Published: 05 October 2010
|
|
|