024PA(66-co-6T)固相缩聚
万利, 冯连芳, 顾雪萍, 张才亮
浙江大学 化学工程与生物工程学系,化学工程联合国家重点实验室,浙江 杭州 310027
Solid state polycondensation of PA(66-co-6T)
WAN Li, FENG Lian-fang, GU Xue-ping, ZHANG Cai-liang
State Key Laboratory of Chemical Engineering, Department of Chemical and Biological Engineering,
Zhejiang University, Hangzhou 310027, China
 全文: PDF(779 KB)   HTML
摘要:

以聚己二酰己二胺-对苯二甲酰己二胺(PA(66-co-6T) )预聚物粉末为原料,研究固相缩聚法(SSP)制备高分子量含芳共聚尼龙.分别考察反应时间、氮气流量、反应温度和芳环含量等对固相缩聚的影响,结果表明:在反应初期,固相缩聚反应速率较快,反应6 h后逐渐减慢;聚合产物的特性黏度随氮气流量增大而增大,当氮气流量大于60 mL·min-1(空速5 min-1)时,产物特性黏度趋于一定值;随反应温度的升高,产物特性黏度增大,但温度超过230 ℃后,产物会发生降解而使特性黏度减小,产物特性黏度随芳环含量的增加而减小, 然而PA(66-co-6T) 的热稳定性提高.

Abstract:

The prepolymer powder of hexamethylene adipamide and hexamethylene terephthalamide was used as a raw material to prepare a high molecular weight aromatic copolyamide PA(66-co-6T) via the solid state polycondensation (SSP) method. The effects of reaction time, nitrogen flow rate, reaction temperature and aromatic ring content on the SSP process were investigated. The results show that the reaction rate is fast during the initial stage of the SSP, while it gradually slows down after 6 hours; the intrinsic viscosity of resulting PA(66-co-6T) increases with the increasing of nitrogen flow rate, and then reach a platform when the nitrogen flow rate is more than 60 mL·min-1 (space velocity at 5 min-1). The intrinsic viscosity of PA(66-co-6T) also goes up with the rising of reaction temperature, and then decreases because of the degradation after reaction temperature is higher than 230 ℃; with the increase of the aromatic ring, the intrinsic viscosity increases of as-synthesized PA(66-co-6T) decreases, and its thermal stability is enhanced.

出版日期: 2014-08-01
:  TQ 316.42  
基金资助:

化学工程联合国家重点实验室资助(SKL-che-09Z02).

通讯作者: 张才亮,男,副教授     E-mail: zhangcailiang@zju.edu.cn
作者简介: 万利(1982—),男,博士生,从事高分子材料合成与加工研究.E-mail: wanli2069@163.com
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章  

引用本文:

万利, 冯连芳, 顾雪萍, 张才亮. 024PA(66-co-6T)固相缩聚[J]. 浙江大学学报(工学版), 10.3785/j.issn.1008-973X.2014.08..

WAN Li, FENG Lian-fang, GU Xue-ping, ZHANG Cai-liang. Solid state polycondensation of PA(66-co-6T). JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 10.3785/j.issn.1008-973X.2014.08..

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2014.08.        http://www.zjujournals.com/eng/CN/Y2014/V48/I8/1522

[1] 王佩刚.含芳环尼龙的合成与表征[D].杭州:浙江大学, 2008.
WANG Pei-gang. Synthesis and characterization of nylon containing aromatic Ring[D]. Hangzhou: Zhejiang University, 2008.
[2] YANG S H, FU P, LIU M Y, et al. Synthesis,characterization and thermal decomposition of poly(decamethylene 2,6-naphthalamide)[J]. Express Polymer Letters, 2010, 4(6): 364-354.
[3] QU L, LONG S R, ZHANG M L, et al. Synthesis and characterization of poly(ethylene terephthalamide/hexa-methylene terephthalamide) [J]. Journal of Macromole-cular Science, Part A: Pure and Applied Chemistry, 2012, 49: 67-72.
[4] HURLEY J M, BERSTED B H. Method for reducing mold deposit formation during molding of polyamide and composition: US, 6,518,341[P], 20030211.
[5] 冈秀明,原哲野,佐佐木繁.半芳香族聚酰胺:中国,1590433[P]. 20050309.
OKA Hideaki, HARA Tetsuno, SASAKI Shige. Semiaromatic polyamide: China, 1590433[P]. 20050309.
[6] 彭治汉,施祖培.塑料工业手册:聚酰胺[M].北京:化学工业出版社,2001: 375-376.
[7] BOUSSIA A C, KONSTANTAKOPOULOU M O, VOUYIOUKA S N, et al. Nanocatalysis in polyamide 6.6 solid state polymerization [J]. Macromolecular Materials and Engineering , 2010 ,296(2): 168-177.
[8] HERRERO M, BENITO P, LABAJOS F M, et al. Struc-tural characterization and thermal properties of polyamide-6.6/Mg,Al/adipate-LDH nanocomposties obtained by solid state polymerization [J]. Jounal of Solid State Chemistry, 2010, 183: 1645-1653.
[9] CAKIR S, NIEUWENHUIZEN M, JANNSSEN P, et al. Incorporation of a semiaromatic nylon salt into polyamide 6 by solid-state or melt polymerization [J]. Polymer, 2012, 53: 5242-5250.
[10] VOUYIOUKA S N, PAPASPYRIDES C D, WEBER J, et al. Polyamide solid state polymerization: Evalu-ation of pertinent kinetic models [J]. Journal of Applied Polymer Science, 2005, 97(2): 671-681.
[11] ZHANG J, SHEN X J, ZHANG J, et al. Experimental and modeling study of the solid state polymeri-zation of poly(ethylene terephthalate) over a wide range of temperatures and particle sizes [J]. Journal of Applied Polymer Science, 2013, 127(5): 3814-3822.
[12] 常静.含芳环聚酰胺的合成与表征[D]. 杭州:浙江大学, 2010.
CHANG Jing. Synthesis and characterization of poly-amide with aromactic ring [D]. Hangzhou: Zhejiang University, 2010.
[13] 刘振鸿.尼龙6固相聚合计算机模拟及其工业化应用研究[D].上海: 东华大学,2005: 27-28.
LIU Zhen-hong. Study on simulation and industrial application of solid-state polymerization of nylon 6[D]. Shanghai: Donghua University, 2005: 27-28.
[14] 王建丰,胡群华,邱高,等.粉末PET固相缩聚的研究[J].合成纤维工业. 2006, 29(1): 1213.
WANG Jian-feng, HU Qun-hua, QIU Gao, et al. Study on solid-state polycondensation of PET particles [J]. China Synthetic Fiber Industry, 2006, 29(1): 12-13.
[15] PAPASPYRIDES C D,VOUYIOUKA S N,BLETSOS I V. New aspects on the mechanism of the solid state polyamidation of PA6,6 salt [J]. Polmer, 2006, 47: 1020-1027.

No related articles found!