PVA与超高摩尔质量PEO复合膜的制备及表征
丁维2, 杜淼1,2, 郑强1,2
1. 浙江大学 高分子合成与功能构造教育部重点实验室,浙江 杭州 310027| 2. 浙江大学 高分子科学与工程学系,浙江 杭州 310027
Preparation and characterization of PVA-ultra-high molecular weight PEO blend films
DING Wei2, DU Miao1,2, ZHENG Qiang1,2
1. Key Laboratory of Macromolecular Synthesis and Functionalization of Ministry of Education, Zhejiang University, Hangzhou  310027, China;2. Department of Polymer Science and Engineering, Zhejiang University, Hangzhou 310027, China
 全文: PDF  HTML
摘要:

将聚乙烯醇(PVA)与超高摩尔质量的聚氧化乙烯(PEO)进行共混,制备了PVA-PEO复合膜,并对混合溶液的流变行为、力学性能及其结晶行为进行了考察.研究发现:PVA水溶液及PVA-PEO混合溶液的稳态流变行为均呈现明显的第一牛顿区、非牛顿区和第二牛顿区.少量PEO的加入使混合溶液的黏度增大,但增加幅度不大|PEO加入后得到的PVA-PEO复合膜的弹性模量、断裂强度及断裂伸长率等力学性能及玻璃化温度均有所提高,且随着PEO质量分数的提高,各项力学性能均得到增强,这与在成膜过程中PEO的加入使PVA的晶区尺寸变小而分布均匀,以及体系中物理交联点增加有关.

Abstract:

Poly vinyl alcohol (PVA) and ultra-high mass weight poly ethylene oxide (PEO) were blended to prepare PVA-PEO blend films. The rheological behavior of the mixed solution, the mechanical properties and crystalline behavior of the blend films were investigated in detail. The steady shear curves of both PVA solution and PVA-PEO mixed solution could be divided into three regions. The viscosity of PVA-PEO mixed solution increase slightly with the introduction of PEO. The results indicated that the elasticity modulus, strength and elongation at break of the films were improved after adding a small amount of ultra-high mass weight PEO and increased with the increase of PEO content. Although the introduction of PEO caused a decline in the crystallinity of PVA, the size of crystalline region of PVA decreased and distributed uniformly. It is believed that the small and uniformly dispersed crystalline regions in fact increase the number of physical crosslinking points and lead to the enhancement of those mechanical performances as well as the glass transition temperature for the blend films.

出版日期: 2013-11-22
:  O 631  
基金资助:

国家自然科学基金资助项目(51173164,20674072)|中央高校基本科研业务费专项基金资助项目(2011QNA4025).

通讯作者: 杜淼,女,副教授.     E-mail: dumiao@zju.edu.cn
作者简介: 丁维(1987—),男,硕士生,主要从事高分子材料共混改性研究.E-mail:butv@zju.edu.cn
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章  

引用本文:

丁维, 杜淼, 郑强. PVA与超高摩尔质量PEO复合膜的制备及表征[J]. J4, 2013, 47(6): 1109-1113.

DING Wei, DU Miao, ZHENG Qiang. Preparation and characterization of PVA-ultra-high molecular weight PEO blend films. J4, 2013, 47(6): 1109-1113.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2013.06.025        http://www.zjujournals.com/eng/CN/Y2013/V47/I6/1109

[1] MANNA U, PATIL S. Borax mediated layer-by-layer self-assembly of neutral poly(vinyl alcohol) and chitosan[J]. Journal of Physical Chemistry B, 2009, 113: 9137-9142.

[2] JEONG J S, MOON J S, JEON S Y, et al. Mechanical properties of electrospun PVA/MWNTs composite nanofibers[J]. Thin Solid Films, 2007, 515: 5136-5141.

 

[3] OGATE N, KAWAKAGE S, OGIHARA T.Poly(vinyl alcohol)-clay and poly(ethylene oxide)-clay blends prepared using water as solvent[J]. Journal of Applied Polymer Science, 1997, 66: 573-581.

[4] MIYAZAKI T, TAKEDA Y, AKANE S, et al. Role of boric acid for a poly(vinyl alcohol) film as a cross-linking agent: Melting behaviors of the films with boric acid[J]. Polymer, 2010, 51: 5539-5549.

[5] KIM J H, SHIN D S, HAN M H, et al. Surface free energy analysis of poly(vinyl alcohol) films having various molecular parameters[J]. Journal of Applied Polymer Science, 2007, 105: 424-428.

[6] WOO J Y, SHIN E J, LEE Y H. Effect of boric acid treatment on the crystallinity and drawability of poly(vinyl alcohol)-iodine complex films[J]. Polymer Bulletin, 2010, 65: 169-180.

[7] LI L, CHEN N, WANG Q. Effect of poly(ethylene oxide) on the structure and properties of poly(vinyl alcohol)[J]. Journal of Polymer Science: Part B: Polymer Physics, 2010, 48: 1946-1954.

[8] SAWATARI C, KONDO T. Interchain hydrogen bonds in blend films of poly(vinyl alcohol) and its derivatives with poly(ethylene oxide)[J]. Macromolecules, 1999, 32: 1949-1955.

[9] ZHANG W, ZHANG Z, WANG X. Investigation on surface molecular conformations and pervaporation performance of the poly(vinyl alcohol) (PVA) membrane[J]. Journal of Colloid and Interface Science, 2009, 333: 346-353.

[10] TERAOKA IWAO. Polymer solutions: an introduction to physical properties[M]. New York: Wiley, 2002: 63-66.

[11] LAI W C, LIAU W B. Study of the miscibility and crystallization behavior of poly(ethylene oxide)/poly(vinyl alcohol) blends[J]. Journal of Applied Polymer Science, 2004, 92: 1562-1568.

[12] 何曼君,陈维孝, 董西侠.高分子物理[M].上海:复旦大学出版社,2005: 114-119.

No related articles found!