浙江大学学报(工学版)  2018, Vol. 52 Issue (12): 2397-2405    DOI: 10.3785/j.issn.1008-973X.2018.12.018
材料科学     
NO3-/NO2-插层MgAl-LDHs在混凝土模拟孔溶液中的阻锈性能
宋迎宾, 徐金霞, 蒋林华, 谭启平, 梅友静
河海大学 力学与材料学院, 江苏 南京 210098
Anti-corrosion performance of NO3-/NO2- intercalation of MgAl-LDHs in simulated concrete pore solution
SONG Ying-bin, XU Jin-xia, JIANG Lin-hua, TAN Qi-ping, MEI You-jing
College of Mechanics and Materials, Hohai University, Nanjing 210098, China
 全文: PDF(9985 KB)   HTML
摘要:

通过共沉淀法合成硝酸根插层镁铝层状双金属氢氧化物MgAl-NO3 LDHs(简称LDHs-NO3),以其为主体,由离子交换制备亚硝酸根插层双金属氢氧化物MgAl-NO2 LDHs(简称LDHs-NO2).通过对比试验,采用等温吸附法、自腐蚀电位和电化学阻抗谱(EIS)研究所制备的LDHs-NO3、LDHs-NO2在混凝土模拟孔溶液中对氯离子的吸附性能及其对钢筋的阻锈作用;采用扫描电镜(SEM)、X射线衍射(XRD)和傅里叶变换红外光谱(FTIR)揭示其阻锈机理.结果表明:LDHs-NO2的最大氯离子吸附量为2.51 mmol/g,与LDHs-NO3相差不大,展现出良好的氯离子吸附性能;LDHs-NO2具有比LDHs-NO3更好的阻锈效果,可以明显提高钢筋在混凝土模拟孔隙液中的临界氯离子浓度值;LDHs-NO2良好的阻锈性能源于对氯离子的吸附和阻锈离子NO2-的释放,对钢筋产生双重阻锈作用,同时有效阻锈成分NO2-逐步释放,可以为钢筋提供长期的保护作用.

Abstract:

Mg-Al-NO2 LDH (LDHs-NO2) was synthesized by anion exchange in the host materia; Mg-Al-NO3 LDH (LDHs-NO3) was prepared by coprecipitation method. By a comparative experiment, the inhibitive effect of LDHs-NO3 and LDHs-NO2 on the corrosion resistance performance of steel in simulated concrete pore solution were investigated by means of chloride equilibrium isotherm, corrosion potential and electrochemical impedance spectroscopy (EIS). Besides, scanning electron microscopy (SEM), X-ray diffraction instrument (XRD) and infrared spectroscopy were applied to observe the morphologies and microstructures of LDHs. Results show that the maximum chloride adsorption capacity of LDHs-NO2 is 2.51 mmol/g, which is similar with that of LDHs-NO3, indicating good adsorption property of chloride ion; LDHs-NO2 has better inhibition effect than LDHs-NO3, which can significantly increase the chloride threshold value of steel in the simulated concrete pore solution. The good anti-corrosion performance of LDHs-NO2 is because of the chloride ions adsorption and the release of NO2- in the interlayer, which provides dual effect of anti-corrosion performance for steel bar. At the same time, the effective corrosion resistance component NO2- is released gradually, which can provide long-term protection for steel bar.

收稿日期: 2017-10-15 出版日期: 2018-12-13
CLC:  TU528.042  
基金资助:

国家自然科学基金面上资助项目(51478164);江苏省自然科学基金资助项目(BK20181306)

通讯作者: 徐金霞,男,教授,博士.orcid.org/0000-0003-4972-2840.     E-mail: xujinxia@hhu.edu.cn
作者简介: 宋迎宾(1991-),男,硕士生,从事混凝土结构耐久性研究.orcid.org/0000-0001-5774-0462.E-mail:2314231473@qq.com
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
作者相关文章  

引用本文:

宋迎宾, 徐金霞, 蒋林华, 谭启平, 梅友静. NO3-/NO2-插层MgAl-LDHs在混凝土模拟孔溶液中的阻锈性能[J]. 浙江大学学报(工学版), 2018, 52(12): 2397-2405.

SONG Ying-bin, XU Jin-xia, JIANG Lin-hua, TAN Qi-ping, MEI You-jing. Anti-corrosion performance of NO3-/NO2- intercalation of MgAl-LDHs in simulated concrete pore solution. JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 2018, 52(12): 2397-2405.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2018.12.018        http://www.zjujournals.com/eng/CN/Y2018/V52/I12/2397

[1] 金伟良, 赵羽习. 混凝土结构耐久性研究的回顾与展望[J]. 浙江大学学报:工学版, 2002, 36(4):27-36 JIN Wei-liang, ZHAO Yu-xi. State-of-the-art on durability of concrete structures[J]. Journal of Zhejiang University:Engineering Science, 2002, 36(4):27-36
[2] 杜荣归, 刘玉, 林昌健. 氯离子对钢筋腐蚀机理的影响及其研究进展[J]. 材料保护, 2006, 39(6):45-50 DU Rong-gui, LIU Yu, LIN Chang-jian. Chloride ions of reinforcing the effect of the corrosion mechanism and its research progress[J]. Materials Protection, 2006, 39(6):45-50
[3] 李伟华, 裴长岭, 何桥, 等. 混凝土中钢筋腐蚀与钢筋阻锈剂[J]. 材料开发与应用, 2007, 22(5):57-60 LI Wei-hua, PEI Chang-ling, HE Qiao, et al. Corrosion of steel bar in concrete and rebar inhibitor[J]. Development and Application of Materials, 2007, 22(5):57-60
[4] GAIDIS J M. Chemistry of corrosion inhibitors[J]. Cement and Concrete Composites, 2004, 26(3):181-189.
[5] SÖYLEV T A, RICHARDSON M G. Corrosion inhibitors for steel in concrete:state-of-the-art report[J]. Construction and Building Materials, 2008, 22(4):609-622.
[6] SARASWATHY V, MURALIDHARAN S, KALYANASUNDARAM R M, et al. Evaluation of a composite corrosion-inhibiting admixture and its performance in concrete under macrocell corrosion conditions[J]. Cement and Concrete Research, 2001, 31(5):789-794.
[7] DE RINCON O T, PEREZ O, PAREDES E, et al. Long-term performance of ZnO as a rebar corrosion inhibitor[J]. Cement and Concrete Composites, 2002, 24(1):79-87.
[8] LIANG H, LI L, POOR N D, et al. Nitrite diffusivity in calcium nitrite-admixed hardened concrete[J]. Cement and Concrete Research, 2003, 33(1):139-146.
[9] YANG Z, FISCHER H, POLDER R. Synthesis and characterization of modified hydrotalcites and their ion exchange characteristics in chloride-rich simulated concrete pore solution[J]. Cement and Concrete Composites, 2014, 47:87-93.
[10] CHEN Y, SHUI Z, CHEN W, et al. Chloride binding of synthetic Ca-Al-NO3 LDHs in hardened cement paste[J]. Construction and Building Materials, 2015, 93:1051-1058.
[11] YOON S, MOON J, BAE S, et al. Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste[J]. Materials Chemistry and Physics, 2014, 145(3):376-386.
[12] 张小娟, 叶陈清, 董士刚, 等. 层状锌铝双金属氢氧化物载酒石酸根对碳钢在中性溶液中的缓蚀作用[C]//第六届全国腐蚀大会论文集. 银川:中国腐蚀防护学会, 2011:582-584. ZHANG Xiao-juan, YE Chen-qing, DONG Shi-gang, et al. Inhibition of tartaric acid-Loaded Zn-Al LDHs on carbon steel in neutral solution[C]//Proceeding of the 6th China Corrosion Conference. Yinchuan:CSCP, 2011:582-584.
[13] XU J, SONG Y, TAN Q, et al. Chloride absorption by nitrate, nitrite and aminobenzoate intercalated layered double hydroxides[J]. Journal of Materials Science, 2017, 52(10):5908-5916.
[14] LI L, SAGUES A A. Chloride corrosion threshold of reinforcing steel in alkaline solutions-open-circuit immersion tests[J]. Corrosion, 2001, 57(1):19-28.
[15] 董泽华, 石维, 郭兴蓬. 用丝束电极研究模拟碳化混凝土孔隙液中缓蚀剂对碳钢局部腐蚀的抑制行为[J]. 物理化学学报, 2011, 27(1):127-134 DONG Ze-hua, SHI Wei, GUO Xing-peng. Localized corrosion inhibition of carbon steel in carbonated concrete pore solution using wire beam electrode[J]. Acta Physico-Chimica Sinica, 2011, 27(1):127-134
[16] 章思颖, 金伟良, 许晨. 混凝土中胺类有机物:胍对钢筋氯盐腐蚀的作用[J]. 浙江大学学报:工学版, 2013, 47(3):449-455 ZHANG Si-ying, JIN Wei-liang, XU Chen, et al. Effectiveness of an amine-based inhibitor-guanidine for steel in chloride-contaminated concrete[J]. Journal of Zhejiang University:Engineering Science, 2013, 47(3):449-455
[17] SHI W, WANG T, DONG Z, et al. Application of wire beam electrode technique to investigate the migrating behavior of corrosion inhibitors in mortar[J]. Construction and Building Materials, 2017, 134:167-175.
[18] SHI W, DONG Z H, KONG D J, et al. Application of wire beam electrode technique to investigate initiation and propagation of rebar corrosion[J]. Cement and Concrete Research, 2013, 48:25-33.
[19] 柳俊哲, 邢锋, 贺智敏, 等. 钢筋混凝土中亚硝酸根与氯离子的临界摩尔比[J]. 硅酸盐学报, 2010, 38(4):615-620 LIU Jun-zhe, XING Feng, HE Zhi-min, et al. Critical mole ratios of nitrite and chloride in reinforced concrete[J]. Journal of the Chinese Ceramic Society, 2010, 38(4):615-620

No related articles found!