水洗及酸洗对毛竹热解产物的影响 
谷双, 路长通, 陈纪忠
浙江大学 化学工程与生物工程学系,浙江 杭州 310027 
Effect of water and acid leaching on pyrolysis products of Phyllostachys pubescens  
GU Shuang, LU Chang-tong, CHEN Ji-zhong
Department of Chemical and Biological Engineering, Zhejiang University, Hangzhou 310027, China 
 全文: PDF  HTML
摘要:

为了探讨竹材资源的加工利用途径, 以毛竹为原料, 分别采用去离子水和质量分数为3%的H2SO4溶液对毛竹进行水洗或酸洗预处理. 采用一喷动式流化床热解炉对毛竹原料和水洗或酸洗预处理样品进行热解实验, 考察升温速率、热解终温温度、水洗或酸洗预处理时间等对热解产物和液相产物组成分布的影响. 热解结果表明, 在不同升温速率和热解终温下, 毛竹热解过程明显不同. 经水洗或酸洗预处理后的毛竹样品热解结果显示, 水洗使毛竹热解生成的固体产物得率降低而液体产物得率升高, 造成了液体产物中有机小分子及苯酚质量分数的升高, 且随水洗时间的延长而加强. 酸洗促进了固体产物的生成, 表明酸具有催化热解过程中脱水反应的作用. 水洗及酸洗显著提高了液体产物中糠醛的质量分数.

Abstract:

In order to develop the utilization technology of bamboo materials, Phyllestachys pubescens was pretreated by water and 3%(mass fraction) sulfuric acid leaching, and then pyrolyzed in a spouted fluidized-bed furnace. The effect of heating rate, pyrolysis temperature, water or acid leaching time on pyrolysis products and component distribution of liquid product was investigated. Pyrolysis results show that Phyllestachys pubescens undergoes different pyrolysis process at different heating rates and pyrolysis temperatures. Product analysis of pretreated sample pyrolysis indicates that water leaching depresses the formation of char and promotes the yield of liquid product, also increases the mass fractions  of organic light molecules and phenol in liquid product. The influence becomes greater as water leaching time is prolonged. Acid leaching promotes the formation of char, which indicates that acid catalyzes dehydration reaction during pyrolysis. Both water and acid leaching obviously increase furfural mass fraction in liquid product.

出版日期: 2013-07-01
:  TQ 6  
通讯作者: 陈纪忠, 男, 教授,博导.     E-mail: chenjz@zju.edu.cn
作者简介: 谷双(1982-), 女, 博士生, 从事生物质热解的研究. E-mail: gushuang1031@yahoo.com.cn
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章  

引用本文:

谷双, 路长通, 陈纪忠. 水洗及酸洗对毛竹热解产物的影响 [J]. J4, 2013, 47(7): 1313-1320.

GU Shuang, LU Chang-tong, CHEN Ji-zhong. Effect of water and acid leaching on pyrolysis products of Phyllostachys pubescens  . J4, 2013, 47(7): 1313-1320.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2013.07.027        http://www.zjujournals.com/eng/CN/Y2013/V47/I7/1313

[1] 浙江省森林资源监测中心, 浙江省林业勘察设计院. 林业在浙江国民经济与社会发展中的地位和作用 [R]. 北京: 中国林业出版社, 1996.
Zhejiang Forest Resources Monitoring Centre, Forestry Survey and Design Institute of Zhejiang Province.The status and role of forestry in the economical and social development of Zhejiang Province [R]. Beijing: China Forestry Publishing House, 1996.
[2] 王娟. 竹子深加工产品的应用 [J]. 资源保护与利用, 2008, 6(2): 72-73.
WANG Juan. Application of bamboo products process deeply [J]. Resource Protection and Application, 2008, 6(2): 72-73.
[3] 周珊, 胡泽友, 喻景权. 竹炭固定化假单胞菌处理含酚废水的研究 [J]. 高校化学工程学报, 2008, 22(5): 889894.
ZHOU Shan, HU Ze-you, YU Jing-quan. Biodegradation of phenol wastewater by pseudomonas sp. immobilized on bamboo-carbon [J]. Journal of Chemical Engineering of Chinese Universities, 2008, 22(5): 889-894.
[4] 欧敏锐, 李忠琴,周训胜, 等. 福建产竹醋液(竹沥)的组分分析 [J]. 福州大学学报:自然科学版, 2003, 31(3): 360-363.
OU Min-rui, LI Zhong-qin, ZHOU Xun-sheng, et al. Analysis of main components of bamboo vinegar produced in Fujian [J]. Journal of Fuzhou University: Natural Science, 2003, 31(3): 360-363.
[5] 曾凯斌, 蒋斌波, 陈纪忠. 竹材热解过程的动力学研究 [J]. 化工学报, 2006, 57(2): 318-323.
ZENG Kai-bin, JIANG Bin-bo, CHEN Ji-zhong. Kinetic of bamboo pyrolysis [J]. Journal of Chemical Industry and Engineering (China), 2006, 57(2): 318-323.
[6] 谷双, 陈纪忠. 竹材热解失重动力学模型研究 [J]. 高校化学工程学报, 2011, 25(2): 231-235.
GU Shuang, CHEN Ji-zhong. Kinetic study of Phyllestachys pubescens pyrolysis [J]. Journal of Chemical Engineeing of Chinese Universities, 2011, 25(2): 231-235.
[7] 杜瑛, 齐卫艳, 苗霞, 等. 毛竹的主要化学成分分析与热解 [J]. 化工学报, 2004, 15(12): 2099-2102.
DU Ying, QI Wei-yan, MIAO Xia, et al. Chemical analysis of pubescens and its pyrolysis [J]. Journal of Chemical Industry and Engineering (China), 2004, 15(12): 2099-2102.
[8] 蒋剑春, 邓先伦, 张燕萍, 等. 竹材热解特性研究 [J]. 林产化学与工业, 2005, 25(B10): 15-18.
JIANG Jian-chun, DENG Xian-lun, ZHANG Yan-ping, et al. Study on the characteristic feature of bamboo pyrolysis [J]. Chemistry and Industry of Forest Products, 2005, 25(B10): 15-18.
[9] 杜瑛. 毛竹的主要成分分析及催化热解研究 [D]. 四川:四川大学, 2005.
DU Ying. Study on the analysis of main components and catalytic pyrolysis of pubescens [D]. Sichuan: Sichuan University, 2005.
[10] 苗霞, 罗嘉, 李桂英, 等. 毛竹在氢气中的催化热解研究 [J]. 化学研究与应用, 2007, 19(5): 507512.
MIAO Xia, LUO Jia, LI Gui-ying, et al. Catalytic pyrolysis of pubescens under H2 flow [J]. Chemical Research and Applications, 2007, 19(5): 507-512.
[11] 苗霞. 分子筛催化毛竹热解研究 [D]. 四川: 四川大学, 2006.
MIAO Xia. Study on the catalytic pyrolysis of pubescens over zeolite [D]. Sichuan: Sichuan University, 2006.
[12] 邓代举, 李圣峰, 李桂英, 等. 聚丙烯和毛竹共热解研究 [J]. 化学研究与应用, 2006, 18(10): 1245-1248.
DENG Dai-ju, LI Sheng-feng, LI Gui-ying, et al. Study on the co-pyrolysis of polypropylene and Phyllostachys pubescens [J]. Chemical Research and Applications, 2006, 18(10): 1245-1248.
[13] PAN W P, GEOFFREY N R. Influence of metal ions on volatile products of pyrolysis of wood [J]. Journal of Analytical and Applied Pyrolysis, 1989, 16(2): 117-126.
[14] JENSEN A, KIM D J, WOJTOWICZ M A, et al. TG-FTIR study of the influence of potassium chloride on wheat straw pyrolysis [J]. Energy and Fuels, 1998, 12(5): 929-938.
[15] VARHEGYI G, ANTAL M J. Simultaneous thermogravimetric mass spectrometric studies of thermal decomposition of biopolymers. 2. Sugar cane bagasse in the presence and absence of catalysts [J]. Energy and Fuels, 1988, 2(3): 273-277.
[16] ANTAL M J, VARHEGYI G. Cellulose pyrolysis kinetics: the current dtate of knowledge [J]. Industrial and Engineering Chemistry Research, 1995, 34(3): 703-717.
[17] MAMLEEV V, BOURBIGOT S, BRAS M L, et al. The facts and hypotheses relating to the phenomenological model of cellulose pyrolysis: interdependence of the steps [J]. Journal of Analytical and Applied Pyrolysis, 2009, 84(1): 1-17.
[18] BRANCA C, GALGANO A, BLASI C, et al. H2SO4-catalyzed pyrolysis of corncobs [J]. Energy and Fuels, 2011, 25(1): 359-369.
[19] DOBELE G, ROSSINSKAJA G, TELYSHEVA G, et al. Cellulose dehydration and depolymerization reactions during pyrolysis in the presence of phosphoric acid [J]. Journal of Analytical and Applied Pyrolysis, 1999, 49(1/2): 307-317.
[20] DOBELE G, MEIER D, FAIX O, et al. Volatile products of catalytic flash pyrolysis of cellulouse [J]. Journal of Analytical and Applied Pyrolysis, 2001, 58-59(1): 453-463.
[21] NOWAKOWSKI D J, WOODBRIDGE C R, JONES J M. Phosphorus catalysis in the pyrolysis behaviour of biomass [J]. Journal of Analytical and Applied Pyrolysis, 2008, 83(2): 1972-04.
[22] 高培基, 刘洁, 张玉忠, 等. 天然纤维素在生物降解过程中超分子结构的变化 [J]. 自然科学进展, 1998, 8(4): 391-397.
GAO Pei-ji, LIU Jie, ZHANG Yu-zhong, et al. Changes in the supermolecular structure of native cellulose during biodegradation [J]. Natural Science Progress, 1998, 8(4): 391-397.
[23] BILBAL R, MILLERA A, ARAUZO J. Product distribution in the flash pyrolysis of lignocellulosic materials in a fluidized bed [J]. Fuel, 1988, 67 (11): 1586-1588.
[24] ALVAREZ P, BLANCO C, GRANDA S M. Improvement of the thermal stability of lignocellulosic materials by treatment with sulphuric acid and potassium hydroxide [J]. Journal of Analytical and Applied Pyrolysis, 2004, 72(1): 131-139.
[25] BRANCA C, BLASI C D. Oxidation characteristics of chars generated from wood impregnated with (NH4)2HPO4 and (NH4)2SO4  [J]. Thermochimica Acta, 2007, 456(2): 120-127.
[26] CHAIWAT W, HASEGAWA I, KORI J, et al. Examination of degree of cross-linking for cellulose precursors pretreated with acid/hot water at low temperature [J]. Industrial and Engineering Chemistry Research, 2008, 47(16): 5948-5956.
[27] KUMAR R, MAGO G, BALAN V, et al. Physical and chemical characterizations of corn stover and poplar solids resulting from leading pretreatment technologies [J]. Bioresource Technology, 2009, 100(17): 3948-3962.
[28] DEMIRBAS A, GULLU D. Acetic acid, methanol and acetone from lignocellosics by pyrolysis [J]. Energy Education Science and Technology, 1998, 1(2): 111-115.
[29] LU Q, XIONG W M, LI W Z, et al. Catalytic pyrolysis of cellulose with sulfated metal oxides: a promising method for obtaining high yield of light furan compounds [J]. Bioresource Technology, 2009, 100 (20): 4871-4876.
[30] MOK W S L, ANTAL M J, SZABO P, et al. Formation of charcoal from biomass in a sealed reactor [J]. Industrial and Engineering Chemistry Research, 1992, 31(4): 1162-1166.
[31] VARHEGYI G, SZABO P, MOK W S L, et al. Kinetics of the thermal decomposition of cellulose in sealed vessels at elevated pressure. effects of the presence of water on the reaction mechanism [J]. Journal of Analytical and Applied Pyrolysis, 1993, 26(3): 159-174.
[32] JAKAB E, LIU K, MEUZALAAR H L C. Thermal decomposition of wood and cellulose in the presence of solvent vapors [J]. Industrial and Engineering Chemistry Research, 1997, 36(6): 2087-2095.                                    

No related articles found!