应变强化奥氏体不锈钢焊接接头冲击试验研究
舒翔宇1,郑津洋1,寿比南2,缪存坚1,黄泽1,郭阿宾1
1.浙江大学 化工机械研究所, 浙江 杭州 310027; 2. 全国压力容器标准化委员会,北京 100029
Experimental study on impact behavior of austenitic stainless
steel welding joints after cold stretching
SHU Xiang-yu1, ZHENG Jin-yang1, SHOU Bi-nan2, MIAO Cun-jian1,
HUANG Ze1, GUO A-bin1
1. Institute of Chemical Machinery and Process Equipment, Zhejiang University, Hangzhou 310027, China;
2. China Standardization Committee on Boilers and Pressure Vessels, Beijing 100029, China
 全文: PDF  HTML
摘要：

为了研究9%应变强化工艺对焊接接头冲击性能的影响,给应变强化奥氏体不锈钢焊接接头冲击试验指标的制定提供依据,以奥氏体不锈钢S30408为研究材料,对9%应变强化前、后焊接接头焊缝区和热影响区的标准尺寸和5 mm厚小尺寸夏比V型缺口试样进行-196 ℃低温冲击试验.研究结果表明：9%应变强化对冲击功与侧向膨胀量在统计学上无影响；试样的冲击功与侧向膨胀量均保持线性关系,且线性关系在应变强化前、后在统计学上无明显差异；除焊缝区标准试样外,其余试样在冲击功满足指标要求时,对应的侧向膨胀量也能满足指标要求；应变强化前、后小尺寸试样冲击功与标准尺寸试样冲击功比值在焊缝区内均大于0.5,在热影响区内均等于0.5.
Abstract:

The influence of 9% cold stretching on impact behavior of welding joints was investigated to provide the basis for establishment of eligible criteria on impact tests for austenitic stainless steel welding joints after cold stretching. Charpy V-notched impact tests of S30408 stainless steel welding joints in welds and HAZs before and after 9% cold stretching with two sizes of specimens (standard specimens and 5 mm sub-sized specimens) were conducted at -196 ℃. Experimental results showed no statistically significant difference between test groups before and after cold stretching. Meanwhile, linear relations between Charpy impact energy (KV) and lateral expansion (LE) with two specimen sizes were confirmed. No statistically significant difference was found in linear relations between test groups before and after cold stretching. When KV meets the requirement of standards and specifications, LE also satisfies the requirements, except for standard specimens from welds. Relations of standard and sub-sized specimens Charpy impact energy were also discussed. Before and after cold stretching, the ratio of energy absorbed in sub-sized specimens to that in standard specimens is greater than 0.5 for welds, and equals to 0.5 for HAZs.
出版日期: 2012-07-01
:  TH 142.1  
基金资助:

国家“十一五”科技支撑计划资助项目(2011BAK06B02-05)；国家国际科技合作项目（2010DFB42960）.
通讯作者: 郑津洋，男，博导.     E-mail: jyzh@zju.edu.cn
作者简介: 舒翔宇(1986-)，男，博士生，从事极端承压设备研究.E-mail：zjushuxy@zju.edu.cn
服务　　
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章　　

引用本文:

舒翔宇,郑津洋,寿比南,缪存坚,黄泽,郭阿宾. 应变强化奥氏体不锈钢焊接接头冲击试验研究[J]. J4, 2012, 46(7): 1162-1167.

SHU Xiang-yu, ZHENG Jin-yang, SHOU Bi-nan, MIAO Cun-jian, HUANG Ze, GUO A-bin. Experimental study on impact behavior of austenitic stainless
steel welding joints after cold stretching. J4, 2012, 46(7): 1162-1167.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2012.07.002    或    http://www.zjujournals.com/eng/CN/Y2012/V46/I7/1162

［1］ 郑津洋, 郭阿宾, 缪存坚, 等. 奥氏体不锈钢深冷容器室温应变强化技术［J］. 压力容器, 2010, 27(8): 28-56．
ZHENG Jinyang, GUO Abin, MIAO Cunjian, et al. Cold stretching technique for austenitic stainless steel cryogenic pressure vessels ［J］.Pressure Vessel Technology, 2010, 27(8): 28-56．
［2］ BRAUTIGAM M, HARING H W, KOPL H. Pressure vessels for cryogenic service: some new aspects of materials and construction ［C］∥The 7th International Conference on Pressure Vessel Technology. Dusseldorf: ［s. n.］, 1992: 887-899．
［3］ SREENIVASAN P R. Charpy energylateral expansion relations for a wide range of steels ［J］. International Journal of Pressure Vessels and Piping, 2006, 83(7): 498-504．
［4］ GB 24511, 承压设备用不锈钢钢板及钢带［S］.北京：中国标准出版社, 2009．
［5］ GB/T 20878, 不锈钢耐热钢牌号及化学成分［S］.北京：中国标准出版社, 2007．
［6］ GB 150, 压力容器［S］.北京：中国标准出版社, 2011．
［7］ ASME Boiler and Pressure Vessel Code Ⅷ Division 1:, Rules for construction of pressure vessels ［S］. New York: ASME, 2010．
［8］ ASME Boiler and Pressure Vessel Code Ⅷ Division 2:, Alternative rules: rules for construction of pressure vessels ［S］. New York: ASME, 2010．
［9］ EN 13445, Unfired pressure vessels［S］. Brussels: European Committee for Standardization, 2009．

［10］ GB/T 2650, 焊接接头冲击试验方法［S］.北京：中国标准出版社, 2008．
［11］ GB/T 229, 金属材料夏比摆锤冲击试验方法［S］.北京：中国标准出版社, 2007．
［12］ NB/T 47016, 承压设备产品焊接试件的力学性能检验［S］. 北京：新华出版社, 2011．
［13］ JIS B8266, Alternative standard for construction of pressure vessels ［S］. Tokyo: JISC, 2003．
［14］ JIS G3460, Steel pipes for low temperature service ［S］. Tokyo: JISC, 2006．
［15］ TOWERS O L. Testing of subsized Charpy specimens. Part 2: the influence of specimen thickness on upper shelf behavior ［J］. Metal Construction, 1986, 18(4): 254R-258R．
［16］ KRAFFT J M, SULLIVAN A M, BOYLE R W. Effect of dimensions on fast fracture instability of notched sheets ［C］∥ Proceedings of the Crack Propagation Symposium. Cranfield: ［s. n.］, 1961: 8-28．
［17］ WALLIN K. Upper shelf energy normalization for subsized CharpyV specimens ［J］. International Journal of Pressure Vessels and Piping, 2001, 78(7): 463-470．
［18］ TOWERS O L. Testing of subsized Charpy specimens. Part 1: the influence of specimen thickness on the ductile/brittle transition ［J］. Metal Construction, 1986, 18(3): 171R-176R．
［19］ BRAMFITT B L, MARDER A R. A study of the delamination behavior of a very lowcarbon steel ［J］. Metallurgical Transaction A, 1977, 8A: 1263-1273．
No related articles found!