Preparation and characterization of nano-composite of TiO2 anatase and hydroxyapatite 
XU Kan1,YANG Qian2,NIE Jing-jing2
（1. Second Affiliated Hospital, School of Medicine, Zhejiang University, Hangzhou 310009, China；
2.Department of Chemistry, Zhejiang University, Hangzhou 310027,China ) 
Download:   PDF(580KB) HTML
Export: BibTeX | EndNote (RIS)      

Abstract  

The nano-composite of TiO2 anatase and hydroxyapatite was prepared via the aqueous reaction of “salt solution” made from (NH4)2HPO4 and Ca(NO3)2 and “ester solution” made from acetic acid and tetrabutyl titanate followed by heating the solid product at 800 ℃ for 4 hours. The obtained white powder sample was characterized by X-ray diffraction, infrared spectrum and transmission electro-microscope (TEM). The infrared spectrum showed two character peaks, which were assigned to TiO2 and PO4-3 group and indicated the composite being formed by TiO2 anatase and hydroxyapatite. The size of the nano-composite is ca. 100 nm in the TEM image. Three additional diffraction peaks appeared between 2θ = 30° and 35° for the composite sample, which may suggest the molecular complex in the interface of TiO2 anatase and hydroxyapatite in the nano-composite．

CLC:  TQ 027.1  
Service
E-mail this article
Add to my bookshelf
Add to citation manager
E-mail Alert
RSS
Articles by authors
Cite this article:

XU Kan, YANG Qian, NIE Jing-Jing. Preparation and characterization of nano-composite of TiO2 anatase and hydroxyapatite . J4, 2009, 43(09): 1719-1722.

URL:

http://www.zjujournals.com/eng/10.3785/j.issn.1008-973X.2009.     OR     http://www.zjujournals.com/eng/Y2009/V43/I09/1719


二氧化钛与羟基磷灰石纳米复合材料制备与表征

通过在水溶液中将由磷酸氢氨和硝酸钙制得的“盐溶液”与由钛酸正丁酯和冰醋酸制得的“酯溶液”反应,并将产物在800 ℃下活化4 h,获得二氧化钛与羟基磷灰石的纳米复合物.用X射线衍射、红外光谱和透射电镜(TEM)对纳米复合物的组成和结构进行了研究.红外光谱显示了TiO2和PO4-3的两个特征峰,证实了纳米复合物由二氧化钛和羟基磷灰石组成.透射电镜表明,羟基磷灰石包覆在二氧化钛微晶颗粒的表面,形成颗粒尺寸约为100 nm的二氧化钛/羟基磷灰石复合物.X射线衍射图谱显示所得的二氧化钛与羟基磷灰石纳米复合物在2θ = 30°～35 °处出现3个新的衍射峰,说明纳米复合物的二氧化钛与羟基磷灰石界面上可能生成了分子复合物.


[1] AYERS R A, SIMSKE S J, NUNES C R, et al. Long-term bone ingrowth and residual microhardness of porous block hydroxyapatite implants in humans
[J]. Journal of Oral and Maxillofacial Surgery, 1998, 56(11): 1297-1301.


[2] MEHLISCH D R, LEIDER A S, ROBERTS W E. Histologic evaluation of the bone/graft interface after mandibular augmentation with hydroxylapatite/ purified fibrillar collagen composite implants
[J]. Oral Surgery, Oral Medicine, Oral Pathology, Oral Radiology and Endodontics, 1990, 70(6): 685-692.


[3] HOLMES R E, WARDROP R W, WOLFORD L M. Hydroxylapatite as a bone graft substitute in orthognathic surgery: histologic and histometric findings
[J]. Journal of Oral and Maxillofacial Surgery, 1988, 46(8): 661-671.


[4] HIYASHI T, KIM Y A, NATSUKI T, et al. Minireview mechanical properties of carbon nanomaterials
[J]. ChemPhysChem, 2007, 8(7):999-1004.


[5] ZHOU Gang, LI Yu-bao, XIAO Wei, et al. Synthesis, characterization and antibacterial activities of a novel nanohydroxyapatite/ zinc oxide complex
[J]. Journal of Biomedical Materials Research Part A, 2007, 85(4): 929-937.


[6] WILLIAM W S. Handbook of standard infrared grating spectra
[M]. Philadelphia: Sadtler Research Laboratories Inc., 1980: 1086.


[7] FACHINFORMATIONSZENTRUM K. Information Services. ICSD
[CP/CD]. Germany:
[s.n.], 2007.


[8] JCPDS-ICDD, JADE Version 5.0
[CP/CD]. Pennsylvania:
[s.n.], 2002.


[9] 汪晓霞,张海黔. 羟基磷灰石晶须的水热法合成及表征
[J]. 南京航空航天大学学报,2005,37(5):611-615.

WANG Xiao-xia, ZHANG Hai-qian. Hydrothermal preparation and characterization of hydroxya patite whiskers
[J]. Journal of Nanjing University of Aeronautics and Astronautics, 2005,37(5):611-615.


[10] NIE X, LEYLAND A, MATHEWS A, et al. Effect of solution pH and electrical parameters on hydroxyapatite coatings deposited by a plasma-asisted electrophoresis technique
[J]. Journal of Biomedical Materials Research Part A, 2001, 57(4): 612-618.


[11] POSNER A S, PERLOFF A, DIORI A F. Refinement of the hydroxyapatite structure
[J]. Acta Crystallographica, 1958, 11(4): 308-309.


[12] 陈治清.口腔材料学
[M]. 3版. 北京:人民卫生出版社,2004: 95.
No related articles found!