Modification of mesoporous activated carbon for adsorption of PCDD/Fs
ZHAO Xi yuan, LI Xiao dong, ZHOU Xu jian, CHEN Tong, LU Sheng yong, CEN Ke fa
State Key Laboratory of Clean Energy Utilization, Zhejiang University, Hangzhou 310027, China
Download:   PDF(1894KB) HTML
Export: BibTeX | EndNote (RIS)      

Abstract  
Commercial wood based activated carbon was modified to prepare specified mesoporous activated carbon by Fe(NO3)3 impregnation coupled with CO2 activation in order to increase adsorption capacity of PCDD/Fs. Process variables such as impregnation ratio, activation temperature and activation time were considered. Results show that when the impregnation ratio is 1%, the temperature is 900 ℃, the rate of CO2 is 0.5 L/min and the activation is 2 hours, the mesopore (2 5 nm) volume of modified activated carbon can reach 0.37 cm3/g and account for 62.1% of the total pore volume. An adsorption generator was applied for the adsorption of PCDD/Fs. Results show that the modified one can have a larger adsorption capacity of PCDD/Fs compared to the original activated carbon. Its toxic equivalent quantity (TEQ) removal efficiency can reach 61.4%, while the original activated carbon is only 43.0%.


Published: 29 October 2015
CLC:  TQ 424  
Cite this article:

ZHAO Xi yuan, LI Xiao dong, ZHOU Xu jian, CHEN Tong, LU Sheng yong, CEN Ke fa. Modification of mesoporous activated carbon for adsorption of PCDD/Fs. JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 2015, 49(10): 1842-1848.

URL:

http://www.zjujournals.com/eng/ 10.3785/j.issn.1008 973X.2015.10.003     OR     http://www.zjujournals.com/eng/Y2015/V49/I10/1842


适于吸附二恶英的中孔活性炭的改性

以商业木质活性炭为原料,通过Fe(NO3)3催化改性结合二次活化的方法得到富含2~5 nm中孔的适于吸附二恶英的活性炭.研究Fe(NO3)3与活性炭的质量浸渍比、改性温度、改性时间对活性炭孔结构变化的影响.结果表明,当改性温度为900 ℃,CO2体积流速为0.5 L/min, 质量浸渍比为1%时催化效果最好,改性2 h后得到的活性炭2~5 nm中孔孔容达到0.37 cm3/g,占总孔容的62.1%.利用浙江大学研制的二恶英发生源系统搭建吸附实验台,吸附数据显示改性后活性炭吸附二恶英的能力明显增强,在同等条件下可以将二恶英毒性当量的移除效率从43.0%增加到61.4%.

[1] OLIE K, VERMEULEN P L, HUTZINGER O. Chlorodibenzo p dioxins and chlorodibenzofurans are trace components of fly ash and flue gas of some municipal incinerators in the Netherlands [J]. Chemosphere, 1977, 6(8): 455-459.
[2] NAGANO S, TAMON H, ADZUMI T, et al. Activated carbon from municipal waste [J]. Carbon, 2010,38(6): 915-920.
[3] CHI K H, CHANG S H, HUANG C H, et al. Partitioning and removal of dioxin like congeners in flue gases treated with activated carbon adsorption [J]. Chemosphere, 2006, 64(9): 1489-1498.
[4] 立本英机,安部郁夫. 活性炭的应用技术:其维持管理及存在问题[M]. 高尚愚,译. 南京: 东南大学出版社, 2002: 278-280.
[5] 马显华,李晓东. 典型种类活性炭吸附二恶英影响因素实验研究[J]. 能源工程, 2013(3): 5054. MA Xian hua, LI Xiao dong. Adsorption behavior of dioxin on specific activated carbons [J]. Energy Engineering, 2013(3): 50-54.
[6] LI Y, LI K. Synthesis of mesoporous carbon by catalytic activation using rare earth elements [J]. Carbon, 2010, 48(13): 3974-3975.
[7] OZAKI J, ENDO N, OHIZUMI W, et al. Novel preparation method for the production of mesoporous carbon fiber from a polymer blend [J]. Carbon, 1997, 35(7): 1031-1033.
[8] CHANG K W, LIM Z Y, DU F Y, et al. Synthesis of mesoporous carbon by using polymer blend as template for the high power supercapacitor [J]. Diamond andRelated Materials, 2009, 18(2): 448-451.
[9] LIU Z C, LING L C, QIAO W M, et al. Preparation of pitch based spherical activated carbon with developed mesopore by the aid of ferrocene [J]. Carbon, 1999,37(4): 663-667.
[10] 李艳秋, 李开喜, 孙国华, 等. 高中孔率活性炭的制备与表征 [J]. 新型炭材料, 2011, 26(2): 130136. LI Yan qiu, LI Kai xi, SUN Guo hua, et al. Synthesis and characterization of activated carbon with a highmesoporosity [J]. New Carbon Materials, 2011,26(2): 130-136.
[11] ZHU Z L, LI A M, YAN L, et al. Preparation ofmesoporous spherical activated carbons with large specific surface area from ion exchange resin having various metals [J]. Advanced Materials Research, 2011, 239: 699-702.
[12] 张香兰,陈清如,徐德平,等. 煤基活性炭上K Cu Fe混合物的催化活化造孔及机理[J]. 天津大学学报, 2013, 46(2): 156161.ZHANG Xiang lan, CHEN Qing ru, XU De ping, et al. Preparation of mesoporous activated carbon by catalytic activation of commercial coal based activated carbon [J]. Journal of Tianjin University, 2013, 46(2): 156-161.
[13] 刘小军,刘朝军,曹远翔,等. 浸渍金属盐二次活化制备中孔沥青基球形活性炭的研究[J]. 离子交换与吸附, 2008, 24(4): 289295.LIU Xiao jun, LIU Chao jun, CAO Yuan xiang, et al. Study of preparation of mesoporous pitch based spherical activated carbon through reactivation by impregnated nitrates [J]. Ion Exchange and Adsorption, 2008, 24(4): 289-295.
[14] QIAO W M, SONG Y, YOON S H, et al. Modification of commercial activated carbon through gasification by impregnated metal salts to develop mesoporous structures [J]. New carbon materials, 2005, 20(3): 198-204.
[15] LEI S, MIYAMOTO J, KANOH H, et al. Enhancement of the methylene blue adsorption rate for ultramicroporous carbon fiber by addition of mesopores [J]. Carbon, 2006, 44(10): 1884-1890.
[16] JI Sha sha, LI Xiao dong, REN Yong, et al. Ozone enhanced oxidation of PCDD/Fs over V2O5 TiO2 based catalyst [J]. Chemosphere, 2013, 929(3): 265-272.
[17] EPA U S. Method 1613, Revision B: tetra through octa chlorinated dioxins and furans by isotope dilution HRGC/HRMS [S]. Washington D.C.:[s.n.], 1994.
[18] LAHAYE J, EHRBURGER P. Fundamental issues in control of carbon gasification reactivity [M]. Dordrecht: Kluwer, 1991.
[19] LIU Z C, LING L C, LU C X, et al. Transformation of doped Fe in pitch sphere in carbonization and activation processes [J]. Fuel, 2000, 79(15): 1991-1996.
[20] LI X, LI Z, LUO L. Adsorption kinetics of dibenzofuran in activated carbon packed bed [J]. Chinese Journal of Chemical Engineering, 2008, 16(2): 203-208.
[21] BLANCO J, MARTIN M P, KNAPP C, et al. Adsorption of traces of chlorinated aromatic hydrocarbons: design parameters formonolithic adsorbents [J]. Environmental Engineering Science, 2000, 17(4): 215-219.
[22] CHANG M B, CHI K H, CHANG CHIEN G P.Evaluation of PCDD/F congener distributions in MWI flue gas treated with SCR catalysts [J]. Chemosphere, 2004, 55(11): 1457-1467.

No related articles found!