奥氏体晶粒尺寸对工艺参数的灵敏度方程及应用
臧勇, 赵泽波, 秦勤, 于洋
北京科技大学 机械工程学院,北京 100083
Sensitivity equations of process parameters for austenite grain size and its application
ZANG Yong, ZHAO Ze-bo, QIN Qin, YU Yang
School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China
 全文: PDF(859 KB)   HTML
摘要：

为了便捷、准确地确定工艺参数对奥氏体晶粒尺寸的影响规律,考虑热加工工艺参数间的耦合关系,基于Hodgson再结晶模型建立奥氏体晶粒尺寸对工艺参数的灵敏度方程,探讨工艺参数对奥氏体晶粒尺寸的影响.研究表明：在单道次热加工过程中,变形速率、变形量、间隙时间、初始晶粒尺寸、间隙温度和变形温度灵敏度依次降低,工艺参数在不同的工艺过程中灵敏度不同；在多道次热加工过程中,工艺参数的灵敏度还与工艺参数所在道次和总道次数有关.H型钢开坯过程灵敏度分析结果表明,温度和后两个道次间隙时间是奥氏体晶粒尺寸的关键影响因素；降低温度并缩短间隙时间可以将H型钢开坯后的奥氏体晶粒尺寸减小26.2%.
Abstract:

The sensitivity equations of process parameters on the austenite grain size were suggested in order to determine the rules affecting austenite grain size quickly and accurately. These equations were based on the Hodgson recrystallization models of low carbon steel, and coupling relationships of processing parameters for hot working were considered in these equations. Results showed that the sensitivities of strain rate, strain, inter pass time, initial grain size, deformation temperature and inter pass temperature successively decreased during single-pass hot processing. The sensitivity values were dependent on the specific process. Results showed that the sensitivities of process parameters were associated with the total pass number of hot working and the specific pass of the process parameters because these parameters were changed during multi-pass hot processing. These achievements were applied to the cogging process of H beam. The sensitivity analysis indicates that the deformation temperature and inter pass time of the last two passes are the key factors affecting on the finishing grain size of H beam. Austenite grain size can be reduced by 26.2% when the deformation temperature is lowered and the inter pass time is shorten.
出版日期: 2015-04-01
:  TG 335  
基金资助:

国家“863”高技术研究发展计划资助项目(2009AA03Z515)
作者简介: 臧勇(1963—),男,教授,博导,从事机械装备行为分析及控制、塑性加工工艺与设备、新型冶金装备及工艺技术的研究. E-mail： yzang@ustb.edu.cn
服务　　
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章　　

引用本文:

臧勇, 赵泽波, 秦勤, 于洋. 奥氏体晶粒尺寸对工艺参数的灵敏度方程及应用[J]. 浙江大学学报(工学版), 10.3785/j.issn.1008-973X.2015.04.008.

ZANG Yong, ZHAO Ze-bo, QIN Qin, YU Yang. Sensitivity equations of process parameters for austenite grain size and its application. JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 10.3785/j.issn.1008-973X.2015.04.008.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2015.04.008    或    http://www.zjujournals.com/eng/CN/Y2015/V49/I4/662

［1］ HODGSON P D, HICKSONM R, GIBBS R K. Ultrafine ferrite in low carbon steel ［J］. Scripta Materialia, 1999, 40(10): 1179-1184.
［2］ HODGSON P D, GIBBS R K. A mathematical model to predict the mechanical properties of hot rolled C-Mn and microalloyed steels ［J］. The Iron and Steel Institute of Japan, 1992, 32(12): 1329-1338.
［3］ SUN Z Q, YANG W Y, QI J J, et al. Deformation enhanced transformation and dynamic recrystallization of ferrite in a low carbon steel during multi-pass hot deformation ［J］. Materials Science and Engineering, 2001, 14(2): 115-201.
［4］ 张云祥. 高强度线材热加工的组织演变和性能预报系统研究［D］. 武汉：华中科技大学, 2010.
ZHANG Yun-xiang. Systematic research of prediction for microstructure evolution and property of high strength wire rods ［D］. Wuhan: Huazhong University of Science and Technology, 2010.
［5］ 贺庆强,袁宝民,张勤河,等.工艺参数对 H 型钢热轧过程奥氏体演化的影响［J］.轧钢,2009, 26(3): 18-21.
HE Qing-qiang, YUAN Bao-min, ZHANG Qin-he, et al. Influence of process parameters on austenite grain evolution during H-beam hot rolling ［J］. Steel Rolling, 2009, 26(3): 18-21.
［6］ 杨王玥, 胡安民, 孙祖庆. 低碳钢奥氏体晶粒尺寸的控制［J］. 金属学报, 2000, 36(10): 1050-1054.
YANG Wang-yue, HU An-min, SUN Zu-qing. Control of austenite grain size in a low carbon steel ［J］. Acta Metallurgica Sinica, 2000, 36(10): 1050-1054.
［7］ 岳重祥, 张立文, 阮金华, 等. 工艺参数对棒材粗轧过程晶粒尺寸影响模拟［J］. 大连理工大学学报, 2011, 51(5): 662-666.
YUE Chong-xiang, ZHANG Li-wen, RUAN Jin-hua, et al. Simulation for influence of technological parameters on grain size during roughing rolling of rod ［J］. Journal of Dalian University of Technology, 2011,  51(5):662-666.
［8］ 李新城, 郭飞, 陈光, 等. 超细晶粒钢热模拟试验组织预测研究［J］. 农业机械学报, 2008(11): 152-155.
LI Xin-cheng, GUO Fei, CHEN Guang, et al. Study on the microstructure prediction of ultrafine grain steel in thermal simulation experiment ［J］. Nongye Jixie Xuebao, 2008(11): 152-155.
［9］ 万德成. X70 管线钢的组织控制与细化工艺研究［D］. 唐山：河北理工大学, 2009.
WAN De-cheng. Research on microstructure control and refinement technology for X70 pipeline steel ［D］. Tangshan: Hebei Polytechnic University, 2009.
［10］ 张鑫强, 徐光, 薛正良, 等. 变形工艺对 CSP 微合金高强度钢组织和性能的影响［J］. 武汉科技大学学报: 自然科学版, 2008, 30(6): 571-573.
ZHANG Xin-qiang, XU Guang, XUE Zheng-liang, et al. Influence of CSP deformation parameters on structure and properties of a microalloyed high strength steel ［J］. Journal of Wuhan University of Science and Technology: Natural Science Edition, 2008, 30(6): 571-573.
［11］ 于永梅, 李长生, 许云波. TSCR工艺参数对Fe-3%Si钢带微观组织的影响［J］.东北大学学报:自然科学版, 2008, 29(4): 529-532.
YU Yong-mei, LI Chang-sheng, XU Yun-bo, et al. Effect of TSCR parameters on microstructure of Fe-3%Si strip ［J］. Journal of Northeastern University: Natural Science, 2008, 29(4): 529-532.
［12］ 李龙,唐正友,丁桦,等.变形制度对低碳锰钢组织性能的影响［J］.材料科学与工艺,2009, 17(3): 373-376.
LI Long, TANG Zheng-you, DING Hua, et al. Influences of deformation parameters on microstructures and mechanical properties of low carbon manganese steel ［J］. Materials Science and Technology, 2009, 17(3): 373-376.
［13］ 张红梅, 许云波, 刘振宇, 等. 变形工艺对热轧双相钢显微组织和性能的影响［J］. 东北大学学报: 自然科学版, 2007, 28(4): 505-509.
ZHANG Hong-mei, XU Yun-bo, LIU Zheng-yu, et al. Deformation effect on microstructure and mechanical properties of hot rolled dual phase steel ［J］. Journal of Northeastern University: Natural Science, 2007, 28(4): 505-509.
［14］ 曹宇. 800H 合金组织演变规律与热加工工艺研究［D］. 沈阳：东北大学, 2011.
CAO Yu. Research of microstructure evolution law and hot working technology for alloy 800H ［D］. Shenyang: Northeastern University, 2011.
［15］ 张志波, 刘清友, 张晓兵, 等. 加热温度对管线钢奥氏体晶粒尺寸和铌固溶的影响［J］. 钢铁研究学报, 2008, 20(10): 36-39.
ZHANG Zhi-bo, LIU Qing-you, ZHANG Xiao-bing, et al. Effect of heating temperature on prior austenite size and solution of Nb in pipeline steel ［J］. Journal of Iron and Steel Research, 2008, 20(10): 36-39.
［16］ 赵玲玲, 安子军, 杜凤山, 等. 热变形对 42CrMo 钢奥氏体晶粒尺寸影响的试验研究［J］. 塑性工程学报, 2010, 17(4): 100-103.
ZHAO Ling-ling, AN Zi-jun, DU Feng-shan, et al. Experimental research on the effect of hot deformation on the growth of austenite grain size of 42CrMo steel ［J］. Journal of Plasticity Engineering, 2010, 17(4): 100-103.
［17］ 高彩茹, 刘慧, 杜林秀, 等. 细晶粒低碳钢的轧制工艺对显微组织的影响［J］. 钢铁研究学报, 2006, 18(9): 32-35.
GAO Cai-ru, LIU Hui, DU Lin-xiu, et al. Effect of rolling parameters on microstructure of low carbon ultra-fine grained steel ［J］. Journal of Iron and Steel Research, 2006, 18(9): 32-35.
［18］ 魏洁,刘正东,唐广波,等. C-Mn钢热连轧再结晶模型的适用性研究［J］. 轧钢, 2006,23(1): 46-51.
WEI Jie, LIU Zheng-dong, TANG Guang-bo, et al. Investigation on applicability assessment of recrystallization models of C-Mn steel during hot rolling ［J］. Steel Rolling, 2006, 23(1): 46-51.
［19］ 邓天勇. 基于组织性能预测的柔性化轧制工艺制定方法 ［D］. 沈阳：东北大学, 2008.
DENG Tian-yong. Methodology of establishing flexible rolling technology based on prediction of microstructure and properties ［D］. Shenyang: Northeastern University, 2008.
［20］ 李立新.热轧板带的数值模拟_组织预报及工艺优化［D］.重庆：重庆大学, 2003.
LI Li-xin. Computer simulation, microstructure prediction and technology optimization of plate and strip hot rolling ［D］. Chongqing: Chongqing University, 2003.
［21］ 管婧. 锻造成形过程微观组织优化设计方法研究［D］.济南：山东大学, 2008.
GUAN Jing. Research on microstructure optimization design methods in forging processes ［D］. Jinan: Shandong University, 2008.
[1] 胡星星,裘乐淼,张树有,张辉.  基于混合响应面法的滚压成型回弹角预测控制及应用[J]. J4, 2013, 47(11): 2010-2019.