J4  2012, Vol. 46 Issue (8): 1407-1411    DOI: 10.3785/j.issn.1008-973X.2012.08.008
机械工程     
电脉冲消除45钢淬火件的残余应力
郑建毅1,2, 何闻1, 施彦彬1
1. 浙江大学 流体传动及控制国家重点实验室,浙江省先进制造技术重点实验室,现代制造工程研究所,
浙江 杭州 310027;2.厦门大学 机电工程系,福建 厦门 361005
Eliminating residual stress in 45 steel quenching specimens
by electrical pulse
ZHENG Jian-yi1,2, HE Wen1, SHI Yan-bin1
1. The State Key Laboratory of Fluid Power Transmission and Control, Zhejiang Province Key Laboratory of Advanced
Manufacturing Technology, Institute of Modern Manufacturing Engineering, Zhejiang University, Hangzhou 310027, China;
2. Department of Mechanical and Electrical Engineering, Xiamen University, Xiamen 361005, China
 全文: PDF  HTML
摘要:

为了研究电脉冲消除金属材料内部残余应力的效果,通过储能电容器放电产生高能电脉冲,对淬火后的45优质碳素结构钢冷轧薄板件进行放电处理,采用小孔法测定电脉冲处理前后试样内残余应力的变化规律.用于电脉冲处理的脉冲电流为指数衰减的振荡波形,同时满足第一个主峰的电流密度为12.2 kA/mm2,单次处理的振荡脉冲持续时间小于0.8 ms.试验结果表明,经过电脉冲处理后,45钢淬火件中2个主方向残余应力的幅值均出现较为显著的降低,且两者都出现均化效果.

Abstract:

In order to investigate the effect of electrical pulse on eliminating residual stress within metallic material, high-energy electrical pulse was generated by discharging with energy-storage capacitors, and was adopted to treat quenching cold-rolled sheet specimens that were made of 45 high-quality carbon structural steel, and the hole-drilling method was taken to determine the change rule of the residual stress within the specimens before and after electropulse treatment.The pulse current used for electropulse treatment had oscillating waveshape with exponential damping, whose first peak of the current density was 12.2 kA/mm2 and oscillating pulse duration of single treatment was less than 0.8ms. The experimental results show that the amplitude of residual stresses in the two principal directions of 45 steel quenching specimens decrease much more significantly after electropulsing treatment and both of them are homogenized.

出版日期: 2012-09-23
:  TG 115|O 342  
基金资助:

国家自然科学基金资助项目(50675200);中央高校基本科研业务费专项资金资助项目(2009QNA4002);浙江省重点科技创新团队建设项目资助项目(2009R50008).

通讯作者: 何闻,男,教授、博导.     E-mail: hewens@263.net
作者简介: 郑建毅(1983—),男,博士、讲师,从事残余应力测量及消除技术、振动计量测试等研究.E-mail: zjy@xmu.edu.cn
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章  

引用本文:

郑建毅, 何闻, 施彦彬. 电脉冲消除45钢淬火件的残余应力[J]. J4, 2012, 46(8): 1407-1411.

ZHENG Jian-yi, HE Wen, SHI Yan-bin. Eliminating residual stress in 45 steel quenching specimens
by electrical pulse. J4, 2012, 46(8): 1407-1411.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2012.08.008        http://www.zjujournals.com/eng/CN/Y2012/V46/I8/1407

[1] HE Wen, REN Yaoxin, CHEN Caijin, et al. Analysis on technology of high frequency vibration stress relief [C]∥ Proceedings of the 7th Annual Conference of ASME Power. Chicago, Lllinois, USA: Power Division, 2005: 119-122.
[2] TROITSKII O A, LIKHTMAN V I.Anisotropy of the effect of electronbeam and αirradiation on the deformation process of zinc single crystals in the brittle state [J].Doklady Akademii Nauk SSSR,1963,148(2): 332-334.
[3] SPRECHER A F,MANNAN S L,CONRAD H.On the mechanisms for the electroplastic effect In Metals [J].Acta Metall,1986,34(7): 1145-1162.
[4] CONRAD H.Effects of electric current on solid state phase transformations in metals [J].Materials Science and Engineering : A,2000,287(2):  227-237.
[5] CONRAD H. Electroplasticity in metals and ceramics [J].Materials Science and Engineering : A,2000, 287(2):  276-287.
[6] 刘志义,刘冰,邓小铁,等.脉冲电流对2091AlLi合金超塑变形机理的影响[J].金属学报,2000,36(9): 944-951.
LIU Zhiyi,LIU Bin,DENG Xiaotie,et al.Effect of current pulse on mechanism of superplastic deformation of 2091 AlLi alloy [J]. Acta Metallrugica Sinica, 2000, 36(9): 944-951.
[7] 李尧,杨贤镛,陈洪,等.脉冲电流对Zn22Al合金超塑性力学行为的影响[J].湖北工学院学报,1995,10(1): 1-3.
LI Yao,YANG Xianyong,CHEN Hong,et al.Effect of electric current pulses on superplastic mechanical behavior of Zn22Al alloy [J].Journal of Hubei Polytechnic University,1995,10(1): 1-3.
[8] 董晓华,候东芳,李尧.直流脉冲电流对7475铝合金超塑性变形中位错运动的影响[J].机械工程材料,2005,29(2): 17-20.
DONG Xiaohua,HOU Dongfang,LI Yao.The effect of direct current pulses on the movement of dislocations inside 74-75 aluminum alloy undergoing superplastic deformation[J].Materials for Mechanical Engineering,2005,29(2): 17-20.
[9] ASTM E 83708. Standard test method for determining residual stresses by the holedrilling straingage method[S].Pennsylvania: ASTM International Standards Worldwide, 2008.
[10] KLIMOV K M,SHNYREV G D,NOVIKOV I I.Electroplasticity of metals [J].Doklady Akademii Nauk SSSR,1974,219(2): 323-324.

No related articles found!