聚二甲基硅氧烷原位固化3D打印装置及工艺
苏炼,封森文,谢英睿,栾丛丛,姚鑫骅
In-situ curing polydimethylsiloxane 3D printer and process
Lian SU,Senwen FENG,Yingrui XIE,Congcong LUAN,Xinhua YAO
表 6
Tab.6
试验因素
$ {{\bar{H}_{\mathrm{s1}}}} $
$ {{\bar{H}_{\mathrm{s2}}}} $
$ {{\bar{H}_{\mathrm{s3}}}} $
$ {{\bar{H}_{\mathrm{s4}}}} $
$ {{\bar{H}_{\mathrm{s5}}}} $
$ {R}_{{{H}}_{\mathrm{s}}} $
打印温度A
365.121
368.574
373.124
427.317
398.866
62.1966
喷嘴气压B
265.976
316.706
407.148
453.379
502.967
236.991
打印速度C
598.998
413.397
344.452
229.840
280.468
369.158
打印层高D
369.916
404.005
373.674
415.317
383.265
45.4006