| Surface treatment of 0Cr19Ni9 stainless steel SMAW joint by plasma melting |
| LUO Wei, LUAN Jing-fei, YAN Mi |
| College of Materials and Chemical Engineering, Zhejiang University, Hangzhou 310027, China |
|
|
|
Abstract Micro-plasma arc surface melting of 0Cr19Ni9 shielded metal arc welding joint with a micro-plasma arc welder produced a thin surface melted layer with a refined microstructure. The surface treatment changed the anodic polarization behavior in 0.5 mol/L H2SO4 solution. The polarization tests showed that for the as-welded joint both the heat-affected zone and the weld metal decreased in resistance to corrosion compared with the as-Received parent material while for the micro-plasma arc surface melted joint the corrosion resistance increased significantly. This increase in corrosion resistance is attributed to the rapid solidification of the melted layer. Rapid solidification of the melted layer refines its microstructure, decreases its microsegregation, and inhibits the precipitation of chromium carbides at the grain boundaries.received parent material while for the micro-plasma arc surface melted joint the corrosion resistance increased significantly. This increase in corrosion resistance is attributed to the rapid solidification of the melted layer. Rapid solidification of the melted layer refines its microstructure, decreases its microsegregation, and inhibits the precipitation of chromium carbides at the grain boundaries.
|
|
Received: 21 January 2001
|
|
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|