煤热解沥青炭化程度对KOH活化制备活性炭孔隙结构的影响
汪岸, 骆仲泱, 方梦祥, 岑建孟, 姚鹏
浙江大学 能源清洁利用国家重点实验室, 浙江 杭州 310027
Influence of carbonization degree of coal pyrolytic pitch on the pore structure of carbon activated with KOH
WANG An, LUO Zhong-yang, FANG Meng-xiang, CEN Jian-meng, YAO Peng
State Key Laboratory of Clean Energy Utilization, Zhejiang University, Hangzhou 310027, China
 全文: PDF(1084 KB)   HTML
摘要:

以煤热解沥青为原料,采用KOH活化法制备活性炭提高附加值.在不同减压蒸馏终温(VDFT)和不同预炭化温度下得到碳质前驱体,研究碳质前驱体的炭化程度对制备的活性炭孔隙结构的影响.研究表明,碳质前驱体合适的炭化程度,即前驱体中适量的挥发分、H原子、表面官能团以及合适的结构排列,有益于KOH活化.减压蒸馏终温为440℃的多联产煤热解沥青活化得到的活性炭比表面积最大,为2 599 m2/g.减压蒸馏终温为360℃的沥青在400℃下炭化2 h,经KOH活化后可以得到比表面积为2 575 m2/g的高比表面积活性炭,但是需要预炭化处理,工艺相对复杂.

Abstract:

The activated carbons (ACs) prepared from coal pyrolytic pitches were activated with KOH to increase the added value of the pitches. The carbon precursors were prepared at different vacuum distillation final temperatures (VDFTs) and different pre-carbonization temperatures. The influence of their carbonization degree on the pore structure of ACs was analyzed. Results show that appropriate carbonization degree, which can be presented by the proper amount of the volatile matter, the H atoms, the surface functional groups in carbon precursors and structure arrangement, is beneficial to the KOH activation. The ACs prepared from pitch with VDFT of 440℃ have the highest specific surface area, which is 2 599 m2/g. The ACs obtained from the pitch treated with VDFT of 360℃, pre-carbonized at 400℃ for 2 h, then activated with KOH have high specific surface area, which is 2 575 m2/g. The method is relatively complicated because of the extra pre-carbonization.

收稿日期: 2017-07-29 出版日期: 2018-08-23
CLC:  TQ522  
基金资助:

国家重点基础研究发展计划资助项目(2017YFB0602800)

通讯作者: 骆仲泱,男,博导.orcid.org/0000-0001-8764-2986.     E-mail: zyluo@zju.edu.cn
作者简介: 汪岸(1993-),女,硕士生,从事煤热解沥青利用研究.orcid.org/0000-0002-7591-7310.E-mail:wanganzju@zju.edu.cn
服务  
把本文推荐给朋友
加入引用管理器
E-mail Alert
作者相关文章  

引用本文:

汪岸, 骆仲泱, 方梦祥, 岑建孟, 姚鹏. 煤热解沥青炭化程度对KOH活化制备活性炭孔隙结构的影响[J]. 浙江大学学报(工学版), 2018, 52(8): 1551-1557.

WANG An, LUO Zhong-yang, FANG Meng-xiang, CEN Jian-meng, YAO Peng. Influence of carbonization degree of coal pyrolytic pitch on the pore structure of carbon activated with KOH. JOURNAL OF ZHEJIANG UNIVERSITY (ENGINEERING SCIENCE), 2018, 52(8): 1551-1557.

链接本文:

http://www.zjujournals.com/eng/CN/10.3785/j.issn.1008-973X.2018.08.015        http://www.zjujournals.com/eng/CN/Y2018/V52/I8/1551

[1] 康东娟, 唐晓龙, 易红宏, 等. 超级活性炭的制备和性能研究及应用现状[J]. 环境科学与技术, 2011, 34(7):110-117 KANG Dong-juan, TANG Xiao-long, YI Hong-hong, et al. Recent advances in research of super activated carbon:property, preparation and application[J]. Environmental Science and Technology, 2011, 34(7):110-117
[2] 肖荣林. H2气氛下碱活化石油焦制备活性炭及连续活化技术开发[D]. 大连:大连理工大学, 2013 XIAO Rong-lin. Preparation of activated carbon from petroleum coke by KOH activation in the presence of hydrogen and technology for the continuous activation[D]. Dalian:Dalian University of Technology, 2013
[3] 齐仲辉, 刘洪波, 东红, 等. 石油焦基高比表面积活性炭制备技术研究[J]. 炭素技术, 2015, 34(2):36-40 QI Zhong-hui, LIU Hong-bo, DONG Hong, et al. Preparative techniques for high surface area activated carbon from petroleum cokes[J]. Carbon Techniques, 2015, 34(2):36-40
[4] VILAPLANA-ORTEGO E, LILLO-RODENAS M A, ALCANIZ-MONGE J, et al. New insights on the direct activation of isotropic petroleum pitch by alkaline hydroxides[J]. Fuel Processing Technology, 2010, 91(2):145-149.
[5] ASENJO N G, BOTAS C, BLANCO C, et al. Synthesis of activated carbons by chemical activation of new anthracene oil-based pitches and their optimization by response surface methodology[J]. Fuel Processing Technology, 2011, 92(10):1987-1992.
[6] BYAMBA-OCHIR N, SHIM W G, BALATHANIG AIMANI M S, et al. Highly porous activated carbons prepared from carbon rich Mongolian anthracite by direct NaOH activation[J]. Applied Surface Science, 2016, 379:331-337.
[7] 舒成, 李克健, 章序文, 等. 原料预处理对氢氧化钾活化法制备活性炭的影响[J]. 炭素技术, 2014, 33(2):5-8 SHU Cheng, LI Ke-jian, ZHANG Xu-wen, et al. Effects of raw material pretreatment on activated carbons prepared with KOH activation[J]. Carbon Techniques, 2014, 33(2):5-8
[8] 李密, 杨琴, 刘守新. 木质原料性质对KOH活化法制备活性炭的影响[J]. 东北林业大学学报, 2009, 37(2):38-39 LI Mi, YANG Qin, LIU Shou-xin. Effect of raw material properties on activated carbon prepared with KOH activation[J]. Journal of Northeast Forestry University, 2009, 37(2):38-39
[9] KROL M, GRYGLEWICZ G, MACHNIKOWSKI J. KOH activation of pitch-derived carbonaceous materials-Effect of carbonization degree[J]. Fuel Processing Technology, 2011, 92(1):158-165.
[10] KIERZEK K, FRACKOWIAK E, LOTA G, et al. Electrochemical capacitors based on highly porous carbons prepared by KOH activation[J]. Electrochimica Acta, 2004, 49(4):515-523.
[11] CHOI P R, LEE E, KWON S H, et al. Characterization and organic electric-double-layer-capacitor application of KOH activated coal-tar-pitch-based carbons:effect of carbonization temperature[J]. Journal of Physics and Chemistry of Solids, 2015, 87:72-79.
[12] ZHAI D, LI B, DU H, et al. The effect of pre-carbonization of mesophase pitch-based activated carbons on their electrochemical performance for electric double-layer capacitors[J]. Journal of Solid State Electrochemistry, 2011, 15(4):787-794.
[13] 王国栋, 邓先伦, 刘晓敏, 等. 天然气吸附存储用高比表面积活性炭研究进展[J]. 生物质化学工程, 2012, 46(3):27-32 WANG Guo-dong, DENG Xian-lun, LIU Xiao-min, et al. Advance research on the preparation of high specific surface area activated carbon for adsorption and storage of natural gas[J]. Biomass Chemical Engineering, 2012, 46(3):27-32
[14] YUAN M, KIM Y, JIA C Q. Feasibility of recycling KOH in chemical activation of oil-sands petroleum coke[J]. The Canadian Journal of Chemical Engineering, 2012, 90(6):1472-1478.
[15] 许斌, 李铁虎. 中间相沥青的调制对纳米级微孔超高表面积活性炭性能的影响[J]. 材料科学与工艺, 2003, 11(4):434-437 XU Bin, LI Tie-hu. Effect of modification of mesophase pitches on performance of ultra-high surface area activated carbons with nanometer level micropore[J]. Materials Science and Technology, 2003, 11(4):434-437
[16] LU C, XU S, WANG M, et al. Effect of pre-oxidation on the development of porosity in activated carbons from petroleum coke[J]. Carbon, 2007, 45(1):206-209.
[17] LU C L, XU S P, GAN Y X, et al. Effect of pre-carbonization of petroleum cokes on chemical activation process with KOH[J]. Carbon, 2005, 43(11):2295-2301.
[18] 朱淮武. 有机分子结构波谱解析[M]. 北京:化学工业出版社, 2005:48-59
[19] YANG Y, LIN Q, HUANG Y, et al. Efficient preparation of mesocarbon microbeads by pyrolysis of coal-tar pitch in the presence of rosin[J]. Journal of Analytical and Applied Pyrolysis, 2011, 91(2):310-315.
[20] 林淑萍, 徐浩, 罗诗渊, 等. 新型沥青基高比表面积活性炭的制备及性能[J]. 化工新型材料, 2015, 43(12):137-139 LIN Shu-ping, XU Hao, LUO Shi-yuan, et al. Preparation and property of pitch-based activated carbons with high surface area[J]. New Chemical Materials, 2015, 43(12):137-139
[21] 林雪. PAN基碳纤维制备过程中纤维的近程有序结构及晶态结构研究[D]. 济南:山东大学, 2014 LIN Xue. Study on short-range ordered structure and crystalline structure of fibers during preparation of PAN-based carbon fibers[D]. Jinan:Shandong University, 2014

No related articles found!